PERMABOND 2010

Main features

  • Thixotropic Vertical-Surface Control
  • Up to 0.5 mm Gap Filling
  • 25 kV/mm Dielectric Strength

Product Description

PERMABOND® 2010 Cyanoacrylate Adhesive is a thixotropic, fast-setting, single-component ethyl cyanoacrylate adhesive designed for vertical, porous, and gap-filling applications. Its semi-gel consistency helps resist running and supports controlled dispensing on metals, plastics, elastomers, ceramics, and wood. At 25 °C, the adhesive provides a viscosity of 2,000–2,500 mPa·s at 20 rpm and 10,000–20,000 mPa·s at 2 rpm, reflecting its thixotropic behavior. It fills gaps up to 0.5 mm and typically reaches handling strength in 10–15 seconds on steel, Buna N rubber, and phenolic, with full strength developing in 24 hours.

Key features

  • Thixotropic semi-gel consistency: Helps prevent running on vertical surfaces while supporting accurate dispensing and placement.
  • Maximum gap-filling capability: Suitable for joints with gaps up to 0.5 mm.
  • Fast fixture performance: Typical handling strength is achieved in 10–15 seconds on steel, Buna N rubber, and phenolic.

Applications / Suitable for

  • Vertical bonding applications
  • Porous substrates
  • Gap-filling joints up to 0.5 mm
  • Bonding metals, plastics, elastomers, ceramics, and wood
  • High-speed industrial assembly
Product Family

PERMABOND 2010

Loading pricing…
TDS, SDS & Technical Documents

Technical Specifications

General Properties
Appearance
Appearance at room temperature.
Liquid
Chemistry Type
Ethyl cyanoacrylate
Color
The color
Colourless
Specific Gravity
Specific gravity (SG) is the ratio of the density of a substance to the density of a reference substance; equivalently, it is the ratio of the mass of a substance to the mass of a reference substance for the same given volume. For liquids, the reference substance is almost always water (1), while for gases, it is air (1.18) at room temperature. Specific gravity is unitless.
1.1
Physical Properties
Viscosity
Viscosity is a measurement of a fluid’s resistance to flow. Viscosity is commonly measured in centiPoise (cP). One cP is defined as the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP. A product like honey would have a much higher viscosity -around 10,000 cPs- compared to water. As a result, honey would flow much slower out of a tipped glass than water would. The viscosity of a material can be decreased with an increase in temperature in order to better suit an application
2,000-2,500 mPa.s mPa.s
Mechanical Properties
Impact Strength
3-5 kJ/m² mm
Thermal Properties
Thermal Conductivity
Thermal conductivity describes the ability of a material to conduct heat. It is required by power packages in order to dissipate heat and maintain stable electrical performance. Thermal conductivity units are [W/(m K)] in the SI system and [Btu/(hr ft °F)] in the Imperial system.
0.1 W/m.K
Electrical Properties
Dielectric Strength
Dielectric strength is measured in kV per mm and is calculated by the Breakdown voltage divided by the thickness of the tested material. Those two properties go hand in hand and while Breakdown voltage is always thickness dependent, dielectric strength is a general material property. As an example, the dielectric strength of Polyimide is 236 kV/mm. If we place 1mm of Polyimide between two electrodes, it will act as an insulator until the voltage between the electrodes reaches 236 kV. At this point it will start acting as a good conductor, causing sparks, potential punctures and current flow.
25 kV/mm
Maximum gap fill
0.5 mm

Additional Information

Technical properties

As-supplied / before-processing properties

Typical uncured and curing properties. Values are guideline information and do not constitute product specifications.

Property Value Unit Method / condition
Chemical composition Ethyl cyanoacrylate — Single-component adhesive
Appearance Colorless semi-gel — Thixotropic consistency
Viscosity 2,000–2,500 mPa·s At 25 °C and 20 rpm
Viscosity 10,000–20,000 mPa·s At 25 °C and 2 rpm
Specific gravity 1.1 — Typical uncured value
Maximum gap fill 0.5 mm Equivalent source value 0.02 in
Fixture time — steel 10–15 s Time to 0.3 N/mm² shear strength
Fixture time — Buna N rubber 10–15 s Time to 0.3 N/mm² shear strength
Full strength 24 h Typical full-strength development
Technical properties

After-processing / final-state properties

Typical cured performance values. Bond strength varies with substrate, surface preparation, joint gap, and curing conditions.

Property Value Unit Method / condition
Shear strength — steel 19–23 N/mm² ISO 4587; equivalent source range 2,800–3,300 psi
Shear strength — aluminum 7–9 N/mm² ISO 4587; equivalent source range 1,000–1,300 psi
Shear strength — zinc 10 N/mm² ISO 4587; equivalent source value 1,500 psi
Shear strength — phenolic 14 N/mm² ISO 4587; equivalent source value 2,000 psi
Impact strength 3–5 kJ/m² ASTM D950
Hardness 85 Shore D ISO 868
Dielectric strength 25 kV/mm Typical cured electrical property
Thermal conductivity 0.1 W/(m·K) Typical cured thermal property