PERMABOND 130UV

Harmonization Code : 3506.10.00.00 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg

PERMABOND 130UV

Main features

  • Rapid UV Bonding Cure
  • 200 mPa s Application Viscosity
  • Under 405 Nm LED Conditions

Product Description

PERMABOND® 130UV Light Cure Cyanoacrylate Adhesive is a low-viscosity, solvent-free, dual-cure adhesive designed for rapid bonding of metals and plastics. It combines conventional moisture-initiated cyanoacrylate curing with UV-light curing, allowing exposed adhesive fillets to become tack-free in seconds while small shadowed areas continue to cure through ambient moisture. The adhesive is yellow before cure and becomes clear in a thin bondline. At 25 °C, its 200 mPa·s viscosity supports controlled dispensing, accurate alignment, and automated application. Depending on the substrate, moisture-cure fixture times range from approximately 3 to 80 seconds, while UV exposure at 405 nm can produce a tack-free surface in 1–5 seconds under the documented lamp conditions.

Key features

  • Dual-cure technology: UV light rapidly cures exposed fillets, while moisture curing supports polymerization in small shadow areas.
  • Fast tack-free performance: Achieves a tack-free surface in ≤1 second at 150 mW/cm² or ≤5 seconds at 25 mW/cm² using a 405 nm spot LED.
  • Reduced bloom and odor: Designed to minimize blooming and improve the finished appearance of transparent or exposed joints.

Applications / Suitable for

  • Bonding opaque substrates with exposed adhesive fillets
  • Bonding through transparent plastic components
  • Automated adhesive dispensing
  • Metal and plastic assembly
  • Applications requiring rapid UV cure with secondary shadow-area cure
Product Family

PERMABOND 130UV

Loading pricing…
TDS, SDS & Technical Documents

Technical Specifications

General Properties
Appearance
Appearance at room temperature.
Liquid
Chemistry Type
Ethyl cyanoacrylate
Color
The color
Yellow before cure Clear in a thin bondline
Specific Gravity
Specific gravity (SG) is the ratio of the density of a substance to the density of a reference substance; equivalently, it is the ratio of the mass of a substance to the mass of a reference substance for the same given volume. For liquids, the reference substance is almost always water (1), while for gases, it is air (1.18) at room temperature. Specific gravity is unitless.
1.1
Physical Properties
Open time
3s minutes
Tack-Free Time
<1s minutes
Viscosity
Viscosity is a measurement of a fluid’s resistance to flow. Viscosity is commonly measured in centiPoise (cP). One cP is defined as the viscosity of water and all other viscosities are derived from this base. MPa is another common unit with a 1:1 conversion to cP. A product like honey would have a much higher viscosity -around 10,000 cPs- compared to water. As a result, honey would flow much slower out of a tipped glass than water would. The viscosity of a material can be decreased with an increase in temperature in order to better suit an application
200 mPa.s

Additional Information

Technical properties

As-supplied / before-processing properties

Typical uncured and curing properties. Values are guideline information and do not constitute product specifications.

Property Value Unit Method / condition
Chemical composition Ethyl cyanoacrylate — Single-component, dual-cure adhesive
Appearance Yellow before cure; clear in a thin bondline — Fluoresces under UV light
Viscosity 200 mPa·s At 25 °C; equivalent to cP
Specific gravity 1.1 — Typical uncured value
Moisture fixture time — NBR 3 s 22 °C and 50% relative humidity
Moisture fixture time — steel 30 s 22 °C and 50% relative humidity
Moisture fixture time — polycarbonate 40 s 22 °C and 50% relative humidity
UV tack-free time ≤1 s 405 nm spot LED at 150 mW/cm²
UV tack-free time ≤5 s 405 nm spot LED at 25 mW/cm²
Technical properties

After-processing / final-state properties

Typical cured performance values. Unless otherwise stated, shear values are based on a 24-hour moisture cure. Results vary with substrate, preparation, bondline, and UV exposure.

Property Value Unit Method / condition
Shear strength — abraded mild steel 12–17 N/mm² ISO 4587; 24-hour moisture cure; equivalent source range 1,740–2,465 psi
Shear strength — stainless steel 14–19 N/mm² ISO 4587; 24-hour moisture cure
Shear strength — aluminum 5–9 N/mm² ISO 4587; 24-hour moisture cure
Shear strength — polycarbonate 6–10 N/mm² ISO 4587; 24-hour moisture cure
Shear strength — PMMA 7–11 N/mm² ISO 4587; 24-hour moisture cure
Shear strength — PVC 8–12 N/mm² ISO 4587; 24-hour moisture cure
Hardness 70–80 Shore D ISO 868
Biocompatibility Cytotoxicity tested — ISO 10993-5; claim requires compliance review