FREKOTE 710-LV
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- Room-Temperature Semi-Permanent Release
- High-Slip High-Gloss Finish
- Controlled Two-Coat Application
Product Description
LOCTITE FREKOTE 710-LV Mold Release Agent is a solvent-based semi-permanent polymer mold release treatment for epoxies, thermosets and prepregs, polyester resins, thermoplastic compounds, and high-performance composites. The clear, colorless liquid has a specific gravity of 0.809 to 0.817 and is applied at 13 to 41 deg C. Two initial coats are used on cleaned, dry molds with 5 to 10 minutes between coats, followed by a 15 to 20 minute final cure at 25 deg C. The cured treatment provides a high-slip, high-gloss release surface with room-temperature cure.
Key features
- Room-temperature semi-permanent release: The polymer treatment cures at room temperature to form a semi-permanent release surface.
- High-slip high-gloss finish: The cured treatment is positioned for high slip and a high-gloss molded finish.
- Controlled two-coat application: The initial mold treatment uses two coats with defined intercoat and final-cure times.
Applications
- Release of epoxies, thermosets, and prepregs
- Release of polyester resins and thermoplastic compounds
- High-performance composite molding
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Thermal Properties
Additional Information
As-supplied / before-processing properties
Typical liquid and application-range data before treatment of the mold surface.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Appearance | Clear, colorless liquid | - | As supplied |
| Chemical type | Solvent-based polymer release agent | - | As supplied |
| Specific gravity | 0.809 to 0.817 | - | Typical liquid value |
| Application temperature | 13 to 41 | deg C | Mold and ambient application range |
| Recommended storage temperature | 8 to 21 | deg C | Store in the recommended range |
After-processing / final-state properties
stated applied-film characteristics and cure conditions for the treated mold surface.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Release-film type | Semi-permanent polymer treatment | - | After the stated coating and cure process |
| Initial coating sequence | 2 | coats | Apply to a cleaned, dry mold |
| Intercoat time | 5 to 10 | min | Between initial coats |
| Final cure | 15 to 20 | min | At 25 deg C |
| Release characteristic | High slip | - | Cured mold-release surface |
| Molded-surface finish | High gloss | - | Release-finish characteristic |